Product Details:
Payment & Shipping Terms:
|
Deflection Temperature T: | ≥75℃ | Melting Point: | 114°C |
---|---|---|---|
Crystallinity: | Between 30~45% | Ash: | ≤0.1% |
Tensile Strength: | ≥25.0 MPa | Biological Analysis Rate: | ≥60% |
High Light: | polybutylene succinate,pbs material |
Bio-based Polymer Materials Polybutylene Succinate Pbs Decomposable
Advantages of the product
Based on the bio-based succinic acid produced by our company as a raw material, the bio-based PBS produced by the processes of esterification and polycondensation is a bio-based polymer material encouraged and advocated by the country. With the disposable products produced by this product, complete biodegradation can be achieved by microorganisms in nature. At present, EU countries, such as France and the United Kingdom, have successively banned the use of non-biodegradable materials and forced the use of biodegradable materials. Therefore, bio-based PBS will become a popular degradable material.
Based on the bio-based succinic acid produced by our company as a raw material, through esterification, condensation and other processes forms Bio-based polybutylene succinate (PBS).
That is a bio-based macromolecular material encouraged and promoted by the state. The disposable products produced by this product can be completely biodegradable through the microbes in nature. At present, eu countries, such as France and the UK, have legislated to ban the use of non-biodegradable materials and to enforce the use of biodegradable materials. Therefore, bio-based PBS will become a popular degradable material.
Application
Can be used to produce environmentally friendly degradable plastic products, agricultural film, disposable medical products, biomedical polymer materials, packaging materials, disposable tableware, cosmetic bottles, bio-fibers, bio-foam materials, bio-nonwovens materials and so on.
Product standards and parameters
No. | Project | Unit | Claim | ||||||
Ⅰ | Ⅱ | Ⅲ | Ⅳ | Ⅴ | |||||
1 | Density,25℃ | standard value | g/cm3 | 1.25 | |||||
Bias | ±0.03 | ||||||||
2 | Melting point Tpm | ℃ | 105~116 | ||||||
3 | Melt mass flow rate (MFR) | Nominal value | g/10min | ≤10 | 10~20 | 20~40 | 40~100 | ≥100 | |
Bias | ±1 | ±2 | ±3 | ±5 | |||||
4 | Water content | % | ≤0.1 (method A and method B); ≤0.2 (method C) | ||||||
5 | Carboxyl content | mol/t | ≤50 | — | — | ||||
6 | Color value | L value | — | — | ≥75 | ||||
A value | Nominal value | — | ≤5 | ||||||
Bias | ±0.5 | ||||||||
B value | Nominal value | — | ≤11 | ||||||
Bias | ±1 | ||||||||
7 | Tensile Strength | MPa | ≥25.0 | ||||||
8 | Nominal strain at break | % | ≥150 | ||||||
9 | Bending strength | MPa | ≥25.0 | ||||||
10 | Flexural modulus | MPa | ≥400 | ||||||
11 | Izod notched impact strength | KJ/m2 | ≥4.0 | ||||||
12 | Deflection temperature T | ℃ | ≥75 | ||||||
13 | Intrinsic viscosity | dL/g | ≥1.75 | 1.63~1.75 | 1.37~1.63 | 1.22~1.37 | |||
14 | Ash | % | ≤0.1 | ||||||
15 | Biological analysis rate | % | ≥60 |