Bio-based Polymer Materials Polybutylene Succinate Fully Biodegradable Polymer
Product description and advantages
White granules, polybutylene succinate (PBS) obtained by the condensation polymerization of succinic acid and butanediol. The resin is milky white, odorless and tasteless. It is easily assimilated by various microorganisms in nature or enzymes in plants and animals. Decomposition, metabolism, and finally decomposition into carbon dioxide and water are typical biodegradable polymer materials. Has good biocompatibility and bioabsorbability; density 1.26g/cm3, melting point 114 °C, according to the level of molecular weight and molecular weight distribution, crystallinity between 30 to 45%.
Polybutylene succinate (PBS) can be used as garbage bags, packaging bags, cosmetics bottles, various plastic cards, baby diapers, agricultural materials, and drug release carrier matrix; there are other related to environmental protection Kinds of plastic products, such as landscaping nets and membranes. Polybutylene succinate (PBS) can be used for packaging, tableware, cosmetics bottles and pharmaceutical bottles, disposable medical supplies, agricultural films, pesticides and fertilizers sustained-release materials, biomedical polymer materials and other fields.
Polybutylene succinate (PBS) is a thermoplastic resin and has good processing properties. It can be processed on ordinary processing equipment. The processing temperature range is 140~260°C. The material must be dried prior to processing. The moisture content must be below 0.02%.
Polybutylene succinate (PBS) can be processed by injection molding, blow molding, blown film, blister, lamination, foaming, spinning and other molding methods.
Polybutylene succinate (PBS) is a polymer with good biodegradability. Compared with polylactic acid, polyhydroxyalkanoate, polycaprolactone and other biodegradable plastics, PBS is relatively low in price. Excellent mechanical properties, good heat resistance, heat distortion temperature close to 100 °C.
Product standards and parameters
|2||Melting point Tpm||℃||105~116|
|3||Melt mass flow rate (MFR)||Nominal value||g/10min||≤10||10~20||20~40||40~100||≥100|
|4||Water content||%||≤0.1 (method A and method B); ≤0.2 (method C)|
|6||Color value||L value||—||—||≥75|
|A value||Nominal value||—||≤5|
|B value||Nominal value||—||≤11|
|7||Tensile Strength||MPa||≥25.0|| || |
|8||Nominal strain at break||%||≥150|| || |
|9||Bending strength||MPa||≥25.0|| || |
|10||Flexural modulus||MPa||≥400|| || |
|11||Izod notched impact strength||KJ/m2||≥4.0|| || |
|12||Deflection temperature T||℃||≥75|| || |
|13||Intrinsic viscosity||dL/g||≥1.75||1.63~1.75||1.37~1.63||1.22~1.37|| |
|15||Biological analysis rate||%||≥60|